Refer above diagram.

$A$ is elastic limit, $B$ is upper yield stress point, $C$ is lower yield stress point, $D$ is ultimate stress point and $E$ is the fracture point.

So, till the point $C$, the material will have elastic property but once crossed, the material would not be able to come back to its original condition. Hence, it will behave as a plastic.